P-85 Anchor
Technical Data
A burned phosphate bonded 85% Alumina brick. This brick will find application in ladle slag lines where a high density and low porisuty brick is needed. |
| Average Properties |
| PCE |
Cone 38 |
| MOR |
4000 PSI |
| Apparent Porosity |
17.5% max |
| Bulk Density |
183 pcf |
| CCC |
20,000 PSI |
Reheat Linear Change
2910°F (1600°C) |
1% expansion |
| |
|
| Chemical Analysis |
| Al2 03 |
83.7% |
| Si 02 |
8.1% |
| Fe2 03 |
1.5% |
| CaO |
.1% |
| Ti 02 |
3.2% |
| MgO |
.2% |
| Alkalies |
.5% |
| P205 |
2.3% |
| |
|
| Data is based on average results of control tests and shoud not be used for specification purposes. Variations in test data result from unusual product size, shape, or method of manuacturing process.
|
| |
|
S-85 Anchor
Technical Data
A ceramic bonded 85% Alumina brick designed for the following applications: Eletric furnace roof, ladle lining, rotary kiln, cement kilns, tundishes. |
| Average Properties |
| PCE |
38 |
| Apparent Porosity |
16% - 18% |
| Bulk Density |
2.80g/cm3 |
| MOR |
17.3 Mpa (2500 PSI) |
| CCC |
67 Mpa (9680 PSI) |
Reheat Linear Change
1500° C x 2 hr |
-.05% |
| Chemical Analysis |
| Al2 O3 |
83.5% |
| Si O2 |
12.5% |
| Fe2 O3 |
1.45% |
| Ti O2 |
1.8% |
| Alkalies |
.75% |
| Test data based on average results of control tests and should not be used for specification purposes. Variations in test data result from unusual product size or manufacturing process. |
| |
|
|
S-80 Anchor
Technical Data
A ceramic bonded 80% Alumina brick designed for the following applications: Electric furnace roof, ladle lining, rotary kiln, cement kilns, tundishes. |
| Average Properties |
| PCE |
37 |
| Apparent Porosity |
17% - 19% |
| Bulk Density |
2.5g/cm3 |
| MOR |
12.5 Mpa (1750 PSI) |
| CCC |
53 Mpa (5000 PSI) |
Reheat Linear Change
1500°C) C x 2 hr |
-.20% |
| Chemical Analysis |
| Al2 03 |
78.0% |
| Si 02 |
18.5% |
| Fe2 03 |
1.45% |
| Ti 02 |
1.8% |
| Alkalies |
.25% |
| Test data based on average results of control tests and should not be used for specification purposes. Variations in test data result from unusual product size or manufacturing process. |
| |
|
S-90 Anchor
Technical Data
A ceramic bonded high strength 85% Alumina brick designed for the following applications: Electric furnace roof, adle lining, rotary kiln, cement kilns, tundishes. |
| Average Properties |
| PCE |
40-41 |
| CCC |
1400-1600 PSI |
| Bulk Density |
185-190 pcf
2.95-3.05g/cm3 |
| MOR |
2800 - 3400 PSI |
| Apparent Porosity |
14.0% - 18.0% |
Reheat Linear Change
3100°F (1705°C) |
+0.00% |
| Chemical Analysis |
| Al2 03 |
89.56% |
| Si O2 |
9.62% |
| Fe2 O3 |
.23% |
| Ti O2 |
.28% |
| CaO |
.06% |
| MgO |
.05% |
| Alkalies |
.20% |
| This data is the average of test results based on 9" brick. Since it is subject to reasonable deviations, it cannot be used for specification purposes. Variations in method of manufacture and in size and shape will reflect on the test data, |
| |
|